倒装焊结构的大规模集成电路焊点失效机理研究

doi:10.16257/j.cnki.1681-1070.2023.0129

电子与封装 ›› 2023, Vol. 23 ›› Issue (10): 100202 . doi: 10.16257/j.cnki.1681-1070.2023.0129

倒装焊结构的大规模集成电路焊点失效机理研究

王欢¹,林瑞仕²,朱旭锋²,胡圣¹,李凌¹

1. 西安微电子技术研究所，西安 710068；2. 北京航天自动控制研究所，北京 1000762

收稿日期:2023-04-20 出版日期:2023-10-31 发布日期:2023-10-31
作者简介:王欢（1996—），女，陕西西安人，硕士，工程师，主要研究方向为电子元器件可靠性试验及寿命评估。

Research on Failure Mechanism of Solder Joints in Large-Scale Integrated Circuits with Flip-Chip Structures

WANG Huan¹, LIN Ruishi², ZHU Xufeng², HU Sheng¹, LI Ling¹

1. Xi’an MicroelectronicTechnology Institute, Xi’an 710068, China; 2.Beijing Aerospace Automatic Control Institute, Beijing 100076, China

Received:2023-04-20 Online:2023-10-31 Published:2023-10-31

摘要/Abstract

摘要： 在倒装焊结构的球栅阵列（BGA）封装大规模集成电路（LSIC）的服役过程中，由于BGA焊球、基板材料和PCB材料的热膨胀系数不同，焊点失效成为倒装焊结构LSIC的主要失效模式。焊点失效与焊料性质、焊接时间和温度、制造中的缺陷等密切相关。结合焊点失效的常见形貌及实例，研究倒装焊结构的LSIC的焊点失效模式及失效机理。针对可能引发失效的因素，提出从工艺到应用的一系列预防措施，对提升该类型电路的可靠性具有指导意义。

关键词: 倒装焊, BGA封装, 焊点失效

Abstract: During the service process of large-scale integrated circuits (LSICs) in ball grid array (BGA) packages with flip-chip structures, solder joint failure is the main failure mode of LSICs with flip-chip structures due to the different thermal expansion coefficients of the BGA solder balls, substrate materials and PCB materials. Solder joint failureis closely related to the solder properties, soldering time and temperature, and manufacturing defects.Combined with the common morphology and examples of the solder joint failure, the failure mode and failure mechanism of solder joints of LSICs with flip-chip structures are investigated. A series of preventive measures from process to application are proposed for the factors those may cause failure, which have strong guiding significance for improving the reliability of this type of circuits.

Key words: flip-chip, BGA packages, solder joint failure

中图分类号:

TN305.94

王欢,林瑞仕,朱旭锋,胡圣,李凌. 倒装焊结构的大规模集成电路焊点失效机理研究[J]. 电子与封装, 2023, 23(10): 100202 .

WANG Huan, LIN Ruishi, ZHU Xufeng, HU Sheng, LI Ling. Research on Failure Mechanism of Solder Joints in Large-Scale Integrated Circuits with Flip-Chip Structures[J]. Electronics & Packaging, 2023, 23(10): 100202 .

[1]	汤姝莉,赵国良,张健,薛亚慧. 倒装焊后清洗工艺及其对底部填充的影响[J]. 电子与封装, 2021, 21(2): 20201-.
[2]	马杰. 钉头法倒装焊技术在声表面波器件生产中的应用[J]. 电子与封装, 2018, 18(2): 13-15.
[3]	文惠东，林鹏荣，练滨浩，王勇，姚全斌. 多次回流对不同成分Sn-Pb凸点IMC生长的影响[J]. 电子与封装, 2016, 16(3): 4-8.

中国半导体行业协会封装分会会刊

中国电子学会电子制造与封装技术分会会刊

倒装焊结构的大规模集成电路焊点失效机理研究

Research on Failure Mechanism of Solder Joints in Large-Scale Integrated Circuits with Flip-Chip Structures

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 3

编辑推荐

Metrics

本文评价